High Modulus Fame Retardance UV Stabilized PC Polycarbonate

Product Description

10% GR PC. Optimum combination of high modulus plus excellent impact strength and flame retardance. UV- stabilized. Internal mold release.

General

Form


Resin Pellets


Filler


10 % Glass Fiber


Feature


Outdoor

   F1

Uses                                          PV Convertor Box             Energy Storage                 smart meter

Physical

Nominal Value

Test Method

Density / Specific Gravity

1.25 g/cm³

 

ASTM D792

Water Absorption(Time 24 hr)

0.12 %

ASTM D570

Moisture Absorption at Equilibrium

0.31 %

ASTM D570

Linear Mold Shrinkage, Flow(Thickness; 3.2 mm)

0.2 - 0.4 %


Hardness, Rockwell M

85

ASTM D785

Hardness, Rockwell R

124

ASTM D785

UV light, water exposure/immersion

f1

UL 746C



Mechanical

Nominal Value

Test Method

Tensile Strength, Break(5 mm/min)

55.0 MPa

ASTM D638-1

Tensile Strength, Yield(5 mm/min)

66.0 MPa

ASTM D638-1

Elongation at Break(5 mm/min)

15 %

ASTM D638-1

Elongation at Yield(5 mm/min)

8.0 %

ASTM D638-1

Flexural Yield Strength(1.3 mm/min;50 mm;span)

103 MPa

ASTM D790

Flexural Modulus(1.3 mm/min;50 mm;span)

3440 MPa

ASTM D790

Izod Impact, Notched(Temperature; 23 °C)

106 J/m

ASTM D256

Izod Impact, Unnotched(Temperature; 23 °C;80x10x3 mm)

2136 J/m

ASTM D4812

Tensile Impact Strength

157 kJ/m²

ASTM D1822S

Dart Drop, Total Energy

101 J

ASTM D3029

Taber Abrasion, mg/1000 Cycles(1 kg;1.0e+3 Cycles;CS- 17 Wheel)

11 mg

ASTM D1044

Thermal

Nominal Value

Test Method

CTE, Flow(Temperature; -40 - 95 °C)

32.4 µm/m-°C

ASTM E831

Specific Heat Capacity

1.21 J/g-°C

ASTM C351

Thermal Conductivity

0.200 W/m-K

ASTM C177

Deflection Temperature

Thickness; 6.4 mm;Pressure; 0.46 MPa

Thickness; 6.4 mm;Pressure; 1.8 MPa

 

146 °C

142 °C

ASTM D648

Vicat Softening Point(Rate B/50)

154 °C

ASTM D1525

UL RTI, Electrical

120 °C

UL 746B

UL RTI, Mechanical with Impact

110 °C

UL 746B