Covestro Makrolon 9417

Form

Resin Pellets

Filler

10 % Glass Fiber

Feature

  High Viscosity

Uses

  PV Convertor Box

  smart meter

  LED housing and base      Energy Storage

Physical

Nominal Value

Test Method

Density / Specific Gravity(23 °C)

1.27 g/cm³

ISO 1183

Apparent Bulk Density, Pellets

0.64 g/cm³

ISO 60

Melt Mass-Flow Rate, MFR(300 °C;1.2 kg)

7.0 g/10min

ISO 1133

Melt Volume-Flow Rate, MVR(300 °C;1.2 kg)

6.00 cm³/10 min

ISO 1133

Molding Shrinkage, Across Flow

0.40 - 0.60 %

ISO 2577

2 mm;500 bar;60x60x2mm;280 °C

0.45 %

ISO 294-4

Molding Shrinkage, Flow

0.40 - 0.60 %

ISO 2577

2 mm;500 bar;60x60x2mm

0.60 %

ISO 294-4

Water Absorption, Saturation(23 °C)

0.26 %

ISO 62

Water Absorption, Equilibrium(50% RH;23 °C)

0.10 %

ISO 62

Ball Indentation Hardness

128 MPa

ISO 2039-1

Tensile Modulus(23 °C)

3800 MPa

ISO 527-2/1

Tensile Stress, Yield(23 °C)

64.0 MPa

ISO 527-2/5

Tensile Stress, Break(23 °C)

45.0 MPa

ISO 527-2/5

Tensile Strain, Yield(23 °C)

4.6 %

ISO 527-2/5

Tensile Strain, Break(23 °C)

15 %

ISO 527-2/5

Tensile creep modulus

1 hr

1.0e+3 hr

3600 MPa

2900 MPa

ISO 899-1

Flexural Modulus(2 mm/min;23 °C)

3600 MPa

ISO 178

Flexural Stress

2 mm/min;23 °C

2 mm/min;3.5% Strain;23 °C

105 MPa

95.0 MPa

ISO 178

Flexural Strain at Flexural Strength(2 mm/min;23 °C)

5.8 %

ISO 178

C harpy Notched Impact Strength, Complete Break(23 °C;3 mm)

10 kJ/m²

ISO 179 1eA

C harpy Unnotched Impact Strength, Complete Break

-60 °C

-30 °C

23 °C

100 kJ/m²

120 kJ/m²

150 kJ/m²

ISO 179 1eU

Notched Izod Impact Strength, Complete Break(23 °C;3 mm)

10 kJ/m²

ISO 180/1A