Covestro Makrolon RW2407
General | |
Form | |
Filler | |
Feature | |
Physical Nominal Value Test Method | |
Density / Specific Gravity(23 °C) 1.24 - 1.34 g/cm³ ISO 1183 | |
Melt Volume-Flow Rate, MVR(300 °C;1.2 kg) 19 cm³/10 min ISO 1133 | |
Mechanical Nominal Value Test Method | |
Tensile Modulus(23 °C) 2500 - 2700 MPa ISO 527-2/1 | |
Tensile Stress, Yield(23 °C) 60.0 MPa ISO 527-2/5 | |
Tensile Stress, Break(23 °C) 50.0 - 60.0 MPa ISO 527-2/5 | |
Tensile Strain, Yield(23 °C) 5.5 % ISO 527-2/5 | |
Tensile Strain, Break(23 °C) 80 - 110 % ISO 527-2/5 | |
Nominal Tensile Strain at Break(23 °C) > 50 % ISO 527-2/5 | |
Flexural Modulus(2 mm/min;23 °C) 2500 - 2750 MPa ISO 178 | |
Flexural Stress ISO 178 | |
2 mm/min;23 °C 96.0 MPa | |
2 mm/min;3.5% Strain;23 °C 75.0 - 80.0 MPa | |
Flexural Strain at Flexural Strength(2 mm/min;23 °C) 6.0 - 6.5 % | ASTM D638;ISO 527-2 |
C harpy Unnotched Impact Strength(23 °C) No Break ISO 179 1eU | |
Notched Izod Impact Strength, Complete Break(23 °C) 15 kJ/m² ISO 180/1A | |
Multi-Axial Instrumented Impact Energy(23 °C) 43.0 - 50.0 J ISO 6603-2 | |
Multi-Axial Instrumented Impact, Peak Force(23 °C) 4800 - 5100 N ISO 6603-2 | |
Thermal | Nominal Value | Test Method |
Vicat Softening Temperature | 144 °C | ISO 306/B50 |
RTI Elec(1.5 mm) | 125 °C | UL 746 |
RTI Imp(1.5 mm) | 115 °C | UL 746 |
RTI Str(1.5 mm) | 125 °C | UL 746 |
Flame Rating, WT 2.7 mm 3 mm 0.75 mm 1.5 mm |
HB HB V-2 V-2 | UL 94 |
Glow Wire Flammability Index 0.75 mm 3 mm |
850 °C 960 °C | IEC 60695-2-12 |
Optical | Nominal Value | Test Method |
Light Reflection(4 mm) | 96 - 97 % | JIS 8722 |
Processing | Nominal Value | |
Drying Temperature - Dry Air Dryer<Injection> | 120 °C | |
Drying Time - Dry Air Dryer<Injection> | 4.0 hr | |
Suggested Max Moisture<Injection> | < 0.020 % | |
Suggested Shot Size<Injection> | 30 - |