Dongguan Forever Co.,Ltd is the manufacture of the China origin cheap UV stablized PC polycarbonate Granules Polymer Resin
EXL1330-XH polycarbonate (PC) siloxane copolymer resin is a UV stabilized opaque material that is suitable for injection molding (IM) and sheet extrusion. It has outstanding performance at extremely low temperatures (-60 C) while maintaining good flow properties for efficient processing. With the potential for shorter IM cycle times compared to regular PC resin, the EXL1330-XH resin is a versatile product available in various opaque colors. It is highly recommended for a wide range of applications.
General | ||||
Form | Resin Pellets | |||
Feature | Low Temperature Outdoor High Impact Excellent Processability Impact |
| ||
Usage | Automotive Industria | Consumer Electrical | Healthcare Building and Construction | |
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.18 1.18 g/cm³ | ASTM D792 ISO 1183 | ||
Melt Flow Rate[MFR](300 °C;1.2 kgf) | 10 g/10min | ASTM D1238 | ||
Water Absorption(23 °C;saturated) | 0.35 % | ISO 62-1 | ||
Moisture Absorption(50% RH;23 °C) | 0.15 % | ISO 62 | ||
Melt Volume Rate, MVR(1.2 kg;MVR at 300 °C) | 9 cm³/10 min | ISO 1133 | ||
UV light, water exposure/immersion | f1 | UL 746C | ||
Mechanical | Nominal Value | Test Method | ||
Izod Impact, Notched 23 °C -30 °C -50 °C 23 °C;6.4 mm | 801 J/m 680 J/m 587 J/m 640 J/m | ASTM D256 | ||
Instrumented Dart Impact, Total Energy(23 °C) | 52 J | ASTM D3763 |
Unnotched Izod Impact Strength unnotched;80*10*3;23 °C 0 unnotched;80*10*3;-30 °C 0 | NB kJ/m² NB kJ/m² | ISO 180/1U |
Notched Izod Impact Strength notched;80*10*3;23 °C 0 notched;80*10*3;-30 °C 0 | 70 kJ/m² 55 kJ/m² | ISO 180/1A |
C harpy Impact, V-Notched 23 °C;Edgew;80*10*3;sp =62mm 0 -30 °C;Edgew;80*10*3;sp =62mm 0 | 75 kJ/m² 60 kJ/m² | ISO 179 1eA |
C harpy Impact, Unnotched 23 °C;Edgew;80*10*3;sp =62mm 0 -30 °C;Edgew;80*10*3;sp =62mm 0 | NB kJ/m² NB kJ/m² | ISO 179 1eU |
Tensile Stress, Yield | ||
50 mm/min;Type I | 58 MPa | ASTM D638 |
50 mm/min | 55 MPa | ISO 527 |
Tensile Stress, Break | ||
50 mm/min;Type I | 61 MPa | ASTM D638 |
50 mm/min | 56 MPa | ISO 527 |
Tensile Strain, Yield | ||
50 mm/min;Type I | 6 % | ASTM D638 |
50 mm/min | 5 % | ISO 527 |
Tensile Strain, Break | ||
50 mm/min;Type I | 130 % | ASTM D638 |
50 mm/min | > 100 % | ISO 527 |
Tensile Modulus | ||
50 mm/min | 2100 MPa | ASTM D638 |
1 mm/min | 2100 MPa | ISO 527 |
Flexural Stress, Yield | ||
1.3 mm/min;50 mm;span | 88 MPa | ASTM D790 |
2 mm/min | 85 MPa | ISO 178 |
Flexural Modulus | ||
1.3 mm/min;50 mm;span | 2060 MPa | ASTM D790 |
2 mm/min | 2100 MPa | ISO 178 |
Ball Indentation Hardness(H358/30) | 90 MPa | ISO 2039-1 |
Thermal | Nominal Value | Test Method |
UL Recognized(≥ 0.8 mm) | HB | UL 94 |
Glow Wire Ignition Temperature [GWIT] 3 mm 1.5 mm 0.8 mm 1 mm | 875 °C 875 °C 875 °C 875 °C | IEC 60695-2-13 |
Glow Wire Flammability Index 3 mm 1.5 mm 1 mm 0.8 mm | 960 °C 960 °C 960 °C 850 °C | IEC 60695-2-12 |
Oxygen Index | 35 % | ISO 4589 |
Vicat Softening Temperature Rate B/50 Rate B/50 Rate B/120 | 143 °C 143 °C 145 °C | ASTM D1525 ISO 306 ISO 306 |
Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa 1.82 MPa;6.4 mm | 134 °C 120 °C 124 °C | ASTM D648 |
CTE, Flow -40 - 40 °C 23°C to 80°C | 6.7e-05 1/°C 7.2e-05 1/°C | ASTM E831 ISO 11359-2 |
CTE, XFlow -40 - 40 °C 23°C to 80°C | 6.7e-05 1/°C 7.2e-05 1/°C | ASTM E831 ISO 11359-2 |
Ball Pressure Test(125°C +/- 2°C) | PASSES | IEC 60695-10-2 |
HDT/Be(Edgew;120*10*4;sp =100mm; 0.45 Mpa) | 136 °C | ISO 75/Be |
Hdt/Ae(1.8 MPa;Edgew;120*10*4;sp =100mm) | 125 °C | ISO 75/Ae |
Relative Temp Index, Elec | 125 °C | UL 746B |
Relative Temp Index, Mechanical with Impact | 115 °C | UL 746B |
Relative Temp Index, Mechanical without Impact | 125 °C | UL 746B |
Electrical | Nominal Value | Test Method |
Comparative Tracking Index, CTI | PLC 3 | UL 746A |
Hot-wire Ignition, HWI( ≥ 0.8 mm) | PLC 0 | UL 746A |
High Amp Arc Ignition, HAI( ≥ 0.8 mm) | PLC 0 | UL 746A |
Processing | Nominal Value | |
Drying Temperature<Injection> | 120 °C | |
Drying Time<Injection> | 3 - 4 hrs | |
Drying Time, Cumulative<Injection> | 48 hrs | |
Maximum Moisture Content<Injection> | 0.02 % | |
Melt Temperature<Injection> | 295 - 315 °C | |
Nozzle Temperature<Injection> | 290 - 310 °C | |
Front, Zone 3 Temperature<Injection> | 295 - 315 °C | |
Middle, Zone 2 Temperature<Injection> | 280 - 305 °C | |
Rear, Zone 1 Temperature<Injection> | 270 - 295 °C | |
Mold Temperature<Injection> | 70 - 95 °C | |
Back Pressure<Injection> | 0.3 - 0.7 MPa | |
Screw Speed <Injection> | 40 - 70 rpm | |
Shot To Cylinder Size<Injection> | 40 - 60 % | |
Vent Depth <Injection> | 0.025 - 0.076 mm | |
Drying Temperature<Sheet Extrusion> | 110 - 120 °C | |
Drying Time<Sheet Extrusion> | 3 - 4 hrs | |
Drying Time, Cumulative<Sheet Extrusion> | 48 hrs | |
Maximum Moisture Content<Sheet Extrusion> | 0.02 % | |
Melt Temperature<Sheet Extrusion> | 245 - 260 °C | |
Barrel - Zone 1 Temperature<Sheet Extrusion> | 250 - 290 °C | |
Barrel - Zone 2 Temperature<Sheet Extrusion> | 245 - 270 °C | |
Barrel - Zone 3 Temperature<Sheet Extrusion> | 225 - 255 °C | |
Adapter Temperature<Sheet Extrusion> | 225 - 255 °C | |
Die Temperature<Sheet Extrusion> | 240 - 260 °C | |
Roll Stack Temperature, Top<Sheet Extrusion> | 75 - 115 °C | |
Roll Stack Temperature, Middle<Sheet Extrusion> | 80 - 125 °C | |
Roll Stack Temperature, Bottom<Sheet Extrusion> | 120 - 145 °C |