UV Stabilized High Flow Impact Modified Injection Molding (IM) Grade Polycarbonate Particles

Dongguan Forever Co.,Ltd is the manufacture of the China origin cheap UV stablized PC polycarbonate Granules Polymer Resin

The 923X-XH resin is a type of injection molding material that has been modified to have high flow and resistance to impacts. It is also UV stabilized, meaning it can withstand exposure to sunlight without degradation. It has been designed to meet UL94 V0 @ 1.5mm flame retardancy standards, using non-bromine and non-chlorine systems. Additionally, it has good ductility at low temperatures and is easy to process, with the potential for faster injection molding cycle times compared to standard polycarbonate materials. 923x resin is available in many different opaque colors and can be used in a wide variety of applications.


General

Form


Resin Pellets



Feature


Non-Chlorinated

Excellent Processability

  Non-Brominated


Low Temperature Impact



Ductile

F1

  High Impact

Usage

  Battery Cases


  Energy Storage

                                            Rail                                                                  


                               PV Convertor Box

Physical

Nominal Value

Test Method

Density / Specific Gravity

1.19 g/cm³

ASTM D792

Melt Mass-Flow Rate, MFR(300 °C;1.2 kg)

16 g/10min

ASTM D1238

Molding Shrinkage, Flow(3.2 mm)

0.40 - 0.80 %

Internal Method

Mechanical

Nominal Value

Test Method

Tensile Modulus(5 mm/min)

2100 MPa

ASTM D638

Tensile Strength, Yield(50 mm/min;Type I)

58.0 MPa

ASTM D638

Tensile Strength, Break(50 mm/min;Type I)

60.0 MPa

ASTM D638

Tensile Elongation, Yield(50 mm/min;Type I)

6.0 %

ASTM D638

Tensile Elongation, Break(50 mm/min;Type I)

110 %

ASTM D638

Flexural Modulus(1.3 mm/min;50 mm;Span)

2400 MPa

ASTM D790

Flexural Strength, Yield(1.3 mm/min;50 mm;Span)

90.0 MPa

ASTM D790

Notched Izod Impact


ASTM D256

-30 °C

650 J/m


23 °C

780 J/m


Instrumented Dart Impact, Total Energy(23 °C)

65.0 J

ASTM D3763



Thermal

Nominal Value

Test Method

Deflection Temperature Under Load, Unannealed(1.8 MPa;3.2 mm)

123 °C

ASTM D648

Vicat Softening Temperature(50 °C/h;50 N;Rate A;Loading 2)

140 °C

ASTM D1525

CLTE, Flow(-40 - 40 °C)

6.1E-5 cm/cm/°C

ASTM E831

CLTE, Transverse(-40 - 40 °C)

6.2E-5 cm/cm/°C

ASTM E831

RTI Elec

125 °C

UL 746

RTI Imp

115 °C

UL 746

RTI Str

120 °C

UL 746

Flame Rating

1.5 mm

3 mm


V-0

5VA

UL 94

Glow Wire Flammability Index(1.5 mm)

960 °C

IEC 60695-2-12

Glow Wire Ignition Temperature [GWIT]

1.5 mm

3 mm


825 °C

825 °C

IEC 60695-2-13

Processing


Nominal Value

Drying Temperature<Injection>


120 °C

Drying Time<Injection>


3.0 - 4.0 hr

Suggested Max Moisture<Injection>


0.020 %

Suggested Shot Size<Injection>


40 - 60 %

Rear Temperature<Injection>


270 - 295 °C

Middle Temperature<injection>


280 - 305 °C

Front Temperature<Injection>


295 - 315 °C

Nozzle Temperature<Injection>


290 - 310 °C

Processing Temp, Melt<Injection>


295 - 315 °C

Mold Temperature<Injection>


70 - 95 °C

Back Pressure<Injection>


0.300 - 0.700 MPa

Screw Speed <Injection>


40 - 70 rpm

Vent Depth <Injection>


0.025 - 0.076 mm