Flame Retardant Easy Mold Release Version PC V0 Plastic Granules PC Resin Price

Dongguan Forever Co.,Ltd is the manufacture of the china origin cheap UV stablized PC polycarbonate Granules Polymer Resin

HF1110-XH is a high flow grade polymer with an easy mold release version. It is specifically designed for applications that require thin wall lighting lenses, data storage components, and safety eyewear lenses.


General

Form


Resin Pellets

Feature


Excellent Processability

                                                                     Appliances            Lighting Applications        Automotive Lighting

Usage                                    

Electronic Displays

  Pharmaceuticals  

  Sporting Goods


                                                                    Automotive Exterior


Automotive Interior


Constraction

Physical

Nominal Value

Test Method

Density / Specific Gravity

1.20 g/cm³

ASTM D792

Melt Mass-Flow Rate, MFR(300 °C;1.2 kg)

25 g/10min

ASTM D1238

Molding Shrinkage, Flow(3.2 mm)

0.50 - 0.70 %

Internal Method

Mechanical

Nominal Value

Test Method

Tensile Strength, Yield(50 mm/min;Type I)

62.0 MPa

ASTM D638

Tensile Strength, Break(50 mm/min;Type I)

65.0 MPa

ASTM D638

Tensile Elongation, Break(50 mm/min;Type I)

120 %

ASTM D638

Flexural Modulus(1.3 mm/min;50 mm;Span)

2300 MPa

ASTM D790

Flexural Strength, Yield(1.3 mm/min;50 mm;Span)

93.0 MPa

ASTM D790

Notched Izod Impact(23 °C)

640 J/m

ASTM D256

Instrumented Dart Impact, Energy at Peak(23 °C)

54.0 J

ASTM D3763

Tensile Impact Strength(Type S)

378 kJ/m²

ASTM D1822

Thermal

Nominal Value

Test Method

Deflection Temperature Under Load, Unannealed(1.8 MPa;3.2 mm)

126 °C

ASTM D648

RTI Elec

130 °C

UL 746

RTI Imp

130 °C

UL 746

RTI Str

130 °C

UL 746

Flame Rating(1.1 mm)

V-2

UL 94



Electrical

Nominal Value

Test Method

Comparative Tracking Index[CTI]

PLC 2

UL 746

High Amp Arc Ignition, HAI, Surface

PLC 1

UL 746

High Voltage Arc Tracking Rate, HVTR

PLC 2

UL 746

Hot-wire Ignition, HWI

PLC 2

UL 746

Optical

Nominal Value

Test Method

Transmittance (2.5e+3 µm)

88.0 %

ASTM D1003

Haze(2.5e+3 µm)

1.00 %

ASTM D1003

Processing


Nominal Value

Drying Temperature<Injection>


120 °C

Drying Time<Injection>


3.0 - 4.0 hr

Suggested Max Moisture<Injection>


0.020 %

Suggested Shot Size<Injection>


40 - 60 %

Rear Temperature<Injection>


250 - 270 °C

Middle Temperature<injection>


260 - 280 °C

Front Temperature<Injection>


270 - 295 °C

Nozzle Temperature<Injection>


265 - 290 °C

Processing Temp, Melt<Injection>


270 - 295 °C

Mold Temperature<Injection>


70 - 95 °C

Back Pressure<Injection>


0.300 - 0.700 MPa

Screw Speed <Injection>


40 - 70 rpm

Vent Depth <Injection>


0.025 - 0.076 mm

Drying Time, Cumulative<Injection>


48 hrs




Inquiry