Injectable UV Stabilized Flame Retardant PC/ABS Resin Plastic Blends

Dongguan Forever Co.,Ltd is the manufacture of the China origin cheap UV stablized PC polycarbonate Granules Polymer Resin

CX7240U-XH is an injectable grade of Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) blend that is UV stabilized and flame retardant. It offers a medium flow rate and does not contain chlorine or bromine. With a UL94 [email protected] flame rating, as well as [email protected] and [email protected] flame ratings, it meets high safety standards. This grade also exhibits improved chemical resistance compared to standard PC/ABS blends, making it suitable for thin wall applications.


General

Form

  Resin Pellets



Feature

  Chemical Resistant   


  Outdoor

Excellent Processability    


Non-Brominated & Non- Chlorinated Flame Retardant

Hydrolysis Resistance


Non-Chlorinated

Usage

  Consumer                         Healthcare                         Electrical


  Building and Construction                       Hydrocarbon and Energy

Physical

Nominal Value

Test Method

Density / Specific Gravity


1.19

1.2 g/cm³


ASTM D792

ISO 1183

Melt Flow Rate[MFR](260 °C;2.16 kgf)

16 g/10min

ASTM D1238

Water Absorption(23 °C;saturated)

0.2 %

ISO 62-1

Moisture Absorption(50% RH;23 °C)

0.1 %

ISO 62

Melt Volume Rate, MVR(2.16 kg;MVR at 260 °C)

15 cm³/10 min

ISO 1133



Mechanical

Nominal Value

Test Method

Izod Impact, Notched

23 °C

-30 °C


500 J/m

100 J/m

ASTM D256

Instrumented Dart Impact, Total Energy(23 °C)

65 J

ASTM D3763

Notched Izod Impact Strength

notched;80*10*3;23 °C 0

notched;80*10*3;-30 °C 0


20 kJ/m²

10 kJ/m²

ISO 180/1A

C harpy Impact, V-Notched

23 °C;Edgew;80*10*3;sp =62mm 0

-30 °C;Edgew;80*10*3;sp =62mm 0


20 kJ/m²

10 kJ/m²

ISO 179 1eA

Tensile Stress, Yield



50 mm/min;Type I

65 MPa

ASTM D638

50 mm/min

65 MPa

ISO 527

Tensile Stress, Break



50 mm/min;Type I

58 MPa

ASTM D638

50 mm/min

50 MPa

ISO 527

Tensile Strain, Yield



50 mm/min;Type I

4.1 %

ASTM D638

50 mm/min

4 %

ISO 527

Tensile Strain, Break



50 mm/min;Type I

100 %

ASTM D638

50 mm/min

90 %

ISO 527

Tensile Modulus



50 mm/min

2950 MPa

ASTM D638

1 mm/min

2530 MPa

ISO 527

Flexural Stress, Yield



1.3 mm/min;50 mm;span

104 MPa

ASTM D790

2 mm/min

96 MPa

ISO 178

Flexural Modulus



1.3 mm/min;50 mm;span

2750 MPa

ASTM D790

2 mm/min

2500 MPa

ISO 178

Thermal

Nominal Value

Test Method





Glow Wire Ignition Temperature [GWIT]

3 mm

2 mm

1.5 mm

0.75 mm


800 °C

800 °C

800 °C

800 °C

IEC 60695-2-13

Glow Wire Flammability Index

3 mm

2 mm

1.5 mm

0.75 mm


960 °C

960 °C

960 °C

960 °C

IEC 60695-2-12

Vicat Softening Temperature

Rate B/50

Rate B/50

Rate B/120


106 °C

110 °C

113 °C


ASTM D1525

ISO 306

ISO 306

Heat Deflection Temperature[HDT], Unannealed

0.45 MPa;3.2 mm

3.2 mm;1.82 MPa

1.82 MPa;6.4 mm


100 °C

89 °C

99 °C

ASTM D648

CTE, Flow

-40 - 40 °C

-40 - 40 °C


5.3E-05 1/°C

5.4E-05 1/°C


ASTM E831

ISO 11359-2

CTE, XFlow

-40 - 40 °C

-40 - 40 °C


6.3e-05 1/°C

6.2e-05 1/°C


ASTM E831

ISO 11359-2

Ball Pressure Test(75°C +/- 2°C)

Pass

IEC 60695-10-2

HDT/Af(1.8)

93 °C

ISO 75/Af

Relative Temp Index, Elec

90 °C

UL 746B

Relative Temp Index, Mechanical with Impact

90 °C

UL 746B



Relative Temp Index, Mechanical without Impact

90 °C

UL 746B

Electrical

Nominal Value

Test Method

Comparative Tracking Index, CTI

PLC 3

UL 746A

Hot-wire Ignition, HWI(0.75 mm)

PLC 3

UL 746A

High Amp Arc Ignition, HAI(0.75 mm)

PLC 0

UL 746A

Processing


Nominal Value

Drying Temperature<Injection>


90 °C

Drying Time<Injection>


4 hrs

Maximum Moisture Content<Injection>


0.04 %

Melt Temperature<Injection>


270 - 300 °C

Nozzle Temperature<Injection>


265 - 300 °C

Front, Zone 3 Temperature<Injection>


265 - 300 °C

Middle, Zone 2 Temperature<Injection>


260 - 300 °C

Rear, Zone 1 Temperature<Injection>


260 - 300 °C

Hopper Temperature<Injection>


60 - 80 °C

Mold Temperature<Injection>


60 - 90 °C

Back Pressure<Injection>


0.3 - 0.7 MPa

Screw Speed <Injection>


40 - 70 rpm

Shot To Cylinder Size<Injection>


40 - 80 %

Vent Depth <Injection>


0.038 - 0.076 mm