Stress Crack Resistance High Quality PC/ABS Factory Direct Resin Raw Material Pellets

Dongguan Forever Co.,Ltd is the manufacture of the China origin cheap UV stablized PC polycarbonate Granules Polymer Resin

HR5007A-XH is a thermoplastic plastic made of PC and ABS alloys. Combining the excellent properties of two materials. It can be widely used in automotive accessories, lampshades, handles, and other components. Its comprehensive performance is good, with high impact strength, chemical stability, and good electrical properties.


General

Form

  Resin Pellets


Feature

  Good Thermal

  Excellent Processability    High Impact

Usage

  Automotive

  Housing

  Automotive Exterior   Electrical

  Automotive Interior

Physical                                                                                 Nominal Value

Test Method

Density / Specific Gravity                                                     1.14 g/cm³

ASTM D792

Melt Mass-Flow Rate, MFR(250 °C;2.16 kg)                        5.3 g/10min

ASTM D1238

Molding Shrinkage - Flow, Injection Molded(23 °C;3.2 mm)

0.50 - 0.80 %

ASTM D955

Mechanical                                                                           Nominal Value

Test Method

Tensile Strength, Yield, Injection molded(50 mm/min;23  56.9 MPa °C;3.2 mm)

ASTM D638

Tensile Elongation, Break, Injection Molded(50 mm/min;23 °C;3.2 mm)

> 100 %

ASTM D638

Flexural Modulus, Injection Molded(10 mm/min;23 °C;3.22110 MPa mm)

ASTM D790

Flexural Strength, Injection Molded(10 mm/min;23 °C;3.277.5 MPa mm;Span)

ASTM D790

Notched Izod Impact, Injection Molded

-30 °C;3.2 mm

23 °C;3.2 mm


490 J/m

640 J/m

ASTM D256

Thermal                                                                                Nominal Value

Test Method

Deflection Temperature Under Load, Unannealed, Injection Molded(1.8 MPa;6.4 mm)

113 °C

ASTM D648

RTI Elec                                                                                   60.0 °C

UL 746

RTI Imp                                                                                  60.0 °C

UL 746

RTI Str                                                                                     60.0 °C

UL 746

Flame Rating

1.6 mm

3 mm


HB

HB

UL 94



Processing

Nominal Value

Drying Temperature<Injection>

80 - 100 °C

Drying Time<Injection>

4.0 - 6.0 hr

Suggested Max Moisture<Injection>

0.020 %

Rear Temperature<Injection>

240 - 270 °C

Middle Temperature<injection>

245 - 275 °C

Front Temperature<Injection>

245 - 275 °C

Nozzle Temperature<Injection>

245 - 275 °C

Processing Temp, Melt<Injection>

250 - 275 °C

Mold Temperature<Injection>

50 - 70 °C

Screw Speed <Injection>

40 - 70 rpm