Polycarbonate Sheet Price/Flame Retardant Reinforced PC/ABS Plastic Raw Materials

Dongguan Forever Co.,Ltd is the manufacture of the China origin cheap UV stablized PC polycarbonate Granules Polymer Resin

GP5106F-XH has high impact resistance, high heat resistance, flame retardancy, reinforcement, and transparency. It also has high impact strength at low temperatures. Indoor UV stability. High thermal deformation temperature and other characteristics.


General

Form                                           Resin Pellets

Filler                                           10 % Glass Fiber

Usage                                         Computer Components       Electrical Engineering            Electrical

Physical                                                                                 Nominal Value                                       Test Method

Density / Specific Gravity                                                     1.25 g/cm³                                             ASTM D792

Melt Mass-Flow Rate, MFR(250 °C;2.16 kg)                        4.0 g/10min                                           ASTM D1238

Molding Shrinkage - Flow, Injection Molded(23 °C;3.2 mm)

0.20 - 0.40 %                                          ASTM D955

Rockwell Hardness, R-Scale, Injection Molded(23 °C)        115                                                         ASTM D785

Mechanical                                                                            Nominal Value                                      Test Method

Tensile Strength, Yield, Injection molded(5 mm/min;23 °C;3.2 mm)

65.7 MPa                                                ASTM D638

Tensile Elongation, Break, Injection Molded(5 mm/min;237.0 %                                                      ASTM D638

°C;3.2 mm)

Flexural Modulus, Injection Molded(1.3 mm/min;23 °C;3.2 mm)

3920 MPa                                               ASTM D790

Flexural Strength, Injection Molded(1.3 mm/min;23 °C;3.2108 MPa                                                 ASTM D790

mm)

Notched Izod Impact, Injection Molded(23 °C;3.2 mm)     69 J/m                                                    ASTM D256

Thermal                                                                                 Nominal Value                                      Test Method

Deflection Temperature Under Load, Unannealed, Injection Molded(1.8 MPa;6.4 mm)

113 °C                                                     ASTM D648

RTI Elec                                                                                   60.0 °C                                                     UL 746

RTI Imp                                                                                   60.0 °C                                                    UL 746

RTI Str                                                                                     60.0 °C                                                     UL 746

Flame Rating                                                                                                                                     UL 94

1.7 mm                                                                                 V-0

3 mm                                                                                    V-0



Processing

Nominal Value

Drying Temperature<Injection>

75 - 85 °C

Drying Time<Injection>

3.0 - 5.0 hr

Suggested Max Moisture<Injection>

< 0.020 %

Rear Temperature<Injection>

220 - 240 °C

Middle Temperature<injection>

235 - 255 °C

Front Temperature<Injection>

250 - 265 °C

Nozzle Temperature<Injection>

250 - 265 °C

Processing Temp, Melt<Injection>

235 - 265 °C

Mold Temperature<Injection>

50 - 80 °C

Back Pressure<Injection>

0.0196 - 0.0588 MPa

Screw Speed <Injection>

40 - 70 rpm