High Quality PC/ABS Particles with Stress Cracking Resistance Factory Direct Resin Raw Material Particles
Dongguan Forever Co.,Ltd is the manufacture of the China origin cheap UV stablized PC polycarbonate Granules Polymer Resin
The RCM6134-XH resin is a high-quality injection moldable PC/ABS blend that includes non-brominated and non-chlorinated flame retardant additives. It is composed of 35% post consumer recycled content and has achieved a UL-94 V0 rating at a thickness of 1.0mm. This resin was specifically developed for thin wall applications that demand superior flow and stiffness properties. However, please note that it has limited availability and is only offered in restricted color options.
General | ||||
Form |
| |||
Feature | 35 % Pcr Non-Chlorinated |
| Non-Brominated & Non- Chlorinated Flame Retardant | |
Usage | Electrical | |||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.22 | ASTM D792 | ||
Melt Flow Rate[MFR](260 °C;2.16 kgf) | 11 g/10min | ASTM D1238 | ||
Resin PelletsMechanical | Nominal Value | Test Method |
Izod Impact, Notched(23 °C) | 300 J/m | ASTM D256 |
Instrumented Dart Impact, Total Energy(23 °C) | 52 J | ASTM D3763 |
Notched Izod Impact Strength(notched;80*10*3;23 °C 0) | 20 kJ/m² | ISO 180/1A |
C harpy Impact, V-Notched(23 °C;Edgew;80*10*4;sp =62 mm 0) | 11 kJ/m² | ISO 179 1eA |
Tensile Stress, Yield | ||
5 mm/min;Type I | 54 MPa | ASTM D638 |
5 mm/min | 56 MPa | ISO 527 |
Tensile Stress, Break | ||
5 mm/min;Type I | 44 MPa | ASTM D638 |
5 mm/min | 48 MPa | ISO 527 |
Tensile Strain, Yield | ||
5 mm/min;Type I | 3.5 % | ASTM D638 |
5 mm/min | 3.4 % | ISO 527 |
Tensile Strain, Break | ||
5 mm/min;Type I | 70 % | ASTM D638 |
5 mm/min | 75 % | ISO 527 |
Tensile Modulus | ||
5 mm/min | 3100 MPa | ASTM D638 |
1 mm/min | 3100 MPa | ISO 527 |
Flexural Stress, Yield | ||
1.3 mm/min;50 mm;span | 90 MPa | ASTM D790 |
2 mm/min | 95 MPa | ISO 178 |
Flexural Modulus | ||
1.3 mm/min;50 mm;span | 3100 MPa | ASTM D790 |
2 mm/min | 3100 MPa | ISO 178 |
Thermal | Nominal Value | Test Method |
UL Recognized ≥ 1 mm ≥ 0.8 mm | V-0 V-1 | UL 94 |
Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa | 88 °C 80 °C | ASTM D648 |
CTE, Flow(23°C to 80°C) | 7.0E-05 1/°C | ISO 11359-2 |
CTE, XFlow(23°C to 80°C) | 8.0e-05 1/°C | ISO 11359-2 |
HDT/Af(1.8) | 81 °C | ISO 75/Af |
Relative Temp Index, Elec | 60 °C | UL 746B |
Relative Temp Index, Mechanical with Impact | 60 °C | UL 746B |
Relative Temp Index, Mechanical without Impact | 60 °C | UL 746B |
Electrical | Nominal Value | Test Method |
Hot-wire Ignition, HWI( ≥ 3 mm) | PLC 2 | UL 746A |
Processing | Nominal Value | |
Drying Temperature<Injection> | 80 - 90 °C | |
Drying Time<Injection> | 3 - 4 hrs | |
Drying Time, Cumulative<Injection> | 8 hrs | |
Maximum Moisture Content<Injection> | 0.04 % | |
Melt Temperature<Injection> | 245 - 275 °C | |
Nozzle Temperature<Injection> | 245 - 275 °C | |
Front, Zone 3 Temperature<Injection> | 245 - 275 °C | |
Middle, Zone 2 Temperature<Injection> | 220 - 265 °C | |
Rear, Zone 1 Temperature<Injection> | 220 - 255 °C | |
Mold Temperature<Injection> | 60 - 80 °C | |
Back Pressure<Injection> | 0.3 - 0.7 MPa | |
Screw Speed <Injection> | 40 - 70 rpm | |
Shot To Cylinder Size<Injection> | 30 - 80 % | |
Vent Depth <Injection> | 0.038 - 0.076 mm |