High Quality Plastics Raw Materials Thermal Conductive Plastics PA6 for LED Light Lamp

Dongguan Forever Co.,Ltd is the manufacture of the China origin cheap UV stablized PC polycarbonate Granules Polymer Resin

Product Description

3-8097 VP-XH type PA6 resin can make strong, hard parts. Isotropic shrinkage properties. Inherently flame retardant. Application areas: Automotive industry, textile machinery, instruments and precision engineering. Typical parts: Electrical and electronic industry parts.

General

Form                                        Resin Pellets

Feature

Thermally

  Conductive(Isolation)

Physical

Nominal Value

Test Method

Density / Specific Gravity

1.56 g/cm³

ISO 1183

Linear Mold Shrinkage

0.2 - 0.5 %


Mechanical

Nominal Value

Test Method

Tensile Strength

140 MPa


Elongation at Break

1.60 %


Modulus of Elasticity

1.6E+4 MPa


Flexural Strength(Strain 2.1 %)

215 MPa


Flexural Modulus

1.4E+4 MPa


C harpy Impact Unnotched(23 °C)

30 kJ/m²

ISO 179 1eU

Thermal

Nominal Value

Test Method

Thermal Conductivity, In Plane(Hot Disk;Parallel 60x60x3 3.50 W/m-K

mm)

Maximum Service Temperature, Air



Continuous

90.0 °C


Short Term

210 °C


Deflection Temperature(Pressure; 1.8 MPa)

200 °C


Electrical

Nominal Value

Test Method

Volume Resistivity(10V)

> = 1.00e+6 ohms ·cm


Surface Resistance(10 V)

> = 1.00e+6 Ohms




Processing

Nominal Value

Nozzle Temperature

270 - 280 °C

Zone 1

250 - 270 °C

Barrel - Zone 2 Temperature

270 - 290 °C

Barrel - Zone 3 Temperature

280 - 300 °C

Melt Temperature

270 °C

Mold Temperature

70.0 - 110 °C

Drying Temperature


Time 10 - 16 hr

75.0 °C

Time 4 - 6 hr

105 °C