C 216 V35 BK Z-XH is an injection-moldable polyamide PA6 compound that is strengthened with 35% glass fiber reinforcement. This grade exhibits impressive mechanical properties and delivers an exceptional balance of thermal and mechanical performance.


General

Form


Resin Pellets


Usage


Furniture



Electrical

White Goods & Small   Appliances




  Wire & Cable Applications 



   

Physical



Nominal Value

Test Method

Density / Specific Gravity



1.38 g/cm³

ISO 1183

Water Absorption(24 hr, 23°C)

0.9 %

ISO 62



Mechanical

Nominal Value

Test Method

Tensile Modulus

1 mm/min/dry

1 mm/min/conditioned


11000 MPa

6500 MPa

ISO 527-1/-2

Stress at break

dry

conditioned


175 MPa

110 MPa

ISO 527-1/-2

Strain at break

dry

conditioned


3.2 %

7 %

ISO 527-1/-2

Flexural Modulus

2 mm/min/dry

2 mm/min/conditioned


10000 MPa

6500 MPa

ISO 178

Flexural Strength

2 mm/min/dry

2 mm/min/conditioned


300 MPa

155 MPa

ISO 178

C harpy Impact Strength, Unnotched

dry; 23 ℃

conditioned; 23


90 kJ/m²

95 kJ/m²

ISO 179 1eU

C harpy Notched Impact Strength

dry; 23 ℃

conditioned; 23


12 kJ/m²

20 kJ/m²

ISO 179 1eA

Notched Izod Impact Strength

dry; 23 ℃

conditioned; 23


15 kJ/m²

28 kJ/m²

ISO 180/1A

Thermal

Nominal Value

Test Method

Melting Temperature(10°C/min)

222 °C

ISO 11357-1

Temp. of deflection under load(1.8 MPa)

210 °C

ISO 75

Flammability

0.75 mm

1.5 mm

3 mm


HB

HB

HB

UL 94

Glow-Wire Flammability, GWFI(1.5 mm)

650 °C

IEC 60695-2-12



Electrical

Nominal Value

Test Method

Volume Resistivity

1E+11 ohms ·cm

IEC 62631-3-1

Surface Resistivity

1E+014 Ohms

IEC 62631-3-1

Comparative Tracking Index(Solution A)

400 V

IEC 60112

Processing


Nominal Value

Drying Temperature(除湿干燥机)


80 °C

Drying Time(除湿干燥机)


2 - 4 h

Suggested Max Moisture


0.2 %

Rear Temperature


230 - 235 °C

Middle Temperature


235 - 240 °C

Front Temperature


240 - 250 °C

Blow Molding Mold Temperature


60 - 90 °C