Dongguan Forever Co.,Ltd is the manufacture of the China origin cheap UV stablized PC polycarbonate Granules Polymer Resin
S3C-XH is a type of Polyamide 6 (Nylon 6) material that can be used for injection molding purposes.
Notable properties of S3C-XH include its resistance to chemicals, as well as its ability to provide good mold release.
This makes it suitable for a variety of applications, including engineering and industrial parts, automotive components,
and electrical or electronic applications.
General | |||
Form | Resin Pellets | ||
Feature | Fuel Resistant Solvent Resistant | Excellent Processability Grease Resistant | |
Usage Plugs | Engineering Parts | Connector | |
Physical | Nominal Value | Test Method | |
Density, dry | 1.13 g/cm³ | ISO 1183 | |
Dry: Water Absorption, Saturation | 8.0 % | ISO 62 | |
Dry: Water Absorption, Equilibrium | 2.5 % | ISO 62 | |
Dry: Viscosity Number | 145 cm³/g | ISO 307;ISO 1628;ISO 1157 | |
Mechanical | Nominal Value | Test Method | |
Dry: Tensile Modulus | 3000 MPa | ISO 527-2 | |
Condition: Tensile Modulus | 1800 MPa | ISO 527-2 | |
Dry: Tensile Stress, Yield | 80.0 MPa | ISO 527-2 | |
Condition: Tensile Stress, Yield | 60.0 MPa | ISO 527-2 | |
Dry: Tensile Strain, Yield | 5.0 % | ISO 527-2 | |
Condition: Tensile Strain, Yield | 20 % | ISO 527-2 | |
Dry: Nominal Tensile Strain at Break | 20 % | ISO 527-2/50 | |
Condition: Nominal Tensile Strain at Break | > 50 % | ISO 527-2/50 | |
Dry: Flexural Modulus | 2500 MPa | ISO 178 | |
Dry: Charpy Notched Impact Strength | ISO 179 1eA | ||
-30 °C | 3.00 kJ/m² | ||
23 °C | 5.00 kJ/m² | ||
Condition: Charpy Notched Impact Strength(23 °C) | 25.0 kJ/m² | ISO 179 1eA | |
Dry: Charpy Impact Strength | ISO 179 1eU | ||
-30 °C | No Break | ||
23 °C | No Break | ||
Condition: Charpy Impact Strength(23 °C) | No Break | ISO 179 1eU |
Thermal | Nominal Value | Test Method |
Dry: Deflection Temperature Under Load 0.45 MPa 1.8 MPa | 200 °C 70.0 °C | ISO 75-2 |
Dry: Melting Temperature, DSC | 260 °C | ISO 3146 |
Electrical | Nominal Value | Test Method |
Dry: Volume Resistivity | 1E+11 ohms ·cm | IEC 60093 |
Condition: Volume resistivity | 1E+8 ohms ·cm | IEC 60093 |
Dry: Dielectric Constant(1.0e+6 Hz) | 3.40 | IEC 60250 |
Condition: Dielectric Constant(1.0e+6 Hz) | 5.00 | IEC 60250 |
Dry: Dissipation Factor(1.0e+6 Hz) | 0.025 | IEC 60250 |
Condition: Dissipation factor(1.0e+6 Hz) | 0.20 | IEC 60250 |
Dry: Comparative Tracking Index | 600 | IEC 60112 |
Processing | Nominal Value | |
Processing Temp, Melt<Injection> | 280 - 300 °C | |
Mold Temperature<Injection> | 70 - 80 °C |