Raw PA6 Material Nylon PA6 Plastic Resin for Injection Raw Material PA6 Polyamide PA6 Price

Dongguan Forever Co.,Ltd is the manufacture of the China origin cheap UV stablized PC polycarbonate Granules Polymer Resin

Excellent fiber nylon 6 staple fiber has excellent comprehensive performance, impact resistance, high strength, durable wear resistance, heat resistance, corrosion resistance, low friction coefficient, excellent elasticity and flexibility, etc., easy to process, widely used in papermaking felts, carpets, Abrasives, conveyor belts, tire cords, and other military, civilian, and industrial applications.


General

Form                                        Resin Pellets

Filler                                         30 % Glass Fiber

Feature                                     Flame Retardant

Uses                                          Automotive                       Engineered                        Electron & electric parts

Physical                                                                                 Nominal Value                                       Test Method

Density / Specific Gravity                                                     1.41 g/cm³                                             ISO 1183

Mold Shrinkage, MD                                                            0.3 %                                                       ISO 294-4

Mold Shrinkage, TD                                                             0.7 %                                                       ISO 294-4

Mechanical                                                                            Nominal Value                                      Test Method

Tensile Strength(20 mm/min)                                             135 MPa                                                 ISO 527-2

Elongation at Break(20 mm/min)                                        2.6 %                                                       ISO 527-2

Flexural Strength(2 mm/min)                                              185 MPa                                                 ISO 178

Flexural Modulus(2 mm/min)                                              7800 MPa                                               ISO 178

Notched Izod Impact Strength                                            10 kJ/m²                                                 ISO 180

Thermal                                                                                 Nominal Value                                      Test Method

Heat Deflection Temperature                                                                                                            ISO 75

0.45 MPa                                                                              210 °C

1.82 MPa                                                                              200 °C

Flammability(1.6 mm)                                                         V-0                                                          UL94

Processing                                                                                                                                           Nominal Value

Drying Temperature                                                                                                                            95 - 110 °C

Drying Time                                                                                                                                       2 - 4 h

Mold Temperature                                                                                                                               65 - 100 °C

Melt Temperature                                                                                                                                230 - 265 °C