PA6 Resin Prices Pellets Plastic Nylon 6 Resin Containing 30% Glass Fiber, 15% PTFE

Dongguan Forever Co.,Ltd is the manufacture of the China origin cheap UV stablized PC polycarbonate Granules Polymer Resin


RFL36-XH compound is a specially formulated material made from Nylon 6 resin with 30% glass fiber and 15% PTFE. 


This grade offers excellent resistance to wear and is specifically designed to withstand heavy use and friction.


General

Form

  Resin Pellets

Filler


30 % Glass Fiber


15 % PTFE


Feature


Abrasion Resistant


Structural

  Internally Lubricated

Usage:                   Consumer                          Electrical                            Building and Construction

Physical

Nominal Value

Test Method

Wear Factor Washer

12 10^-10 in^5-min/ft-lb-hr

ASTM D3702

Modified: Manual

Dynamic Cof

0.59

ASTM D3702

Modified: Manual

Density / Specific Gravity

1.51 g/cm³

ISO 1183

Water Absorption(24 hrs;23 °C)

1.34 %

ISO 62-1

Moisture Absorption(50% RH;23 °C)

0.46 %

ISO 62

Melt Volume Rate, MVR(MVR at 275°C/5 kg)

15 - 20 cm³/10 min

ISO 1133

Mold Shrinkage, Flow(24 hrs)

0.2 - 0.5 %

ISO 294

Mold Shrinkage, XFlow(24 hrs)

0.8 - 1.2 %

ISO 294



Mechanical                                                                           Nominal Value

Test Method

Notched Izod Impact Strength(notched;80*10*3;-40 °C 0)12 kJ/m²

ISO 180/1A

Izod Impact, Unnotched(80*10*4;23 °C)                             84 kJ/m²

ISO 180/1U

Unnotched Izod Impact Strength(unnotched;80*10*4;-4074 kJ/m²

°C 0)

ISO 180/1U

Izod Impact, Notched(80*10*4;23 °C)                                 16 kJ/m²

ISO 180/1A

Tensile Stress, Break(5 mm/min)                                         166 MPa

ISO 527

Tensile Strain, Break(5 mm/min)                                         2.6 %

ISO 527

Flexural Stress, Yield

2 mm/min

2 mm/min;60°C

2 mm/min;100 °C

2 mm/min;150°C

2 mm/min;200°C


234 MPa

179 MPa

131 MPa

96 MPa

83 MPa

ISO 178

Flexural Stress, break(2 mm/min)                                        277 MPa

ISO 178

Flexural Strain, Break

2 mm/min

2 mm/min;60°C

2 mm/min;100 °C

2 mm/min;150°C

2 mm/min;200°C


4.1 %

6.1 %

6.6 %

5.6 %

6.3 %

ISO 178

Flexural Modulus

2 mm/min

2 mm/min;60°C

2 mm/min;100 °C

2 mm/min;150°C

2 mm/min;200°C


9100 MPa

5300 MPa

4200 MPa

3500 MPa

3100 MPa

ISO 178




Inquiry