Balanced Flowability And Impact Strength ABS Plastic Raw Material Particles PC ABS Composite Resin Particles

Dongguan Forever Co.,Ltd is the manufacture of the China origin cheap UV stablized PC polycarbonate Granules Polymer Resin

Non-chlorinated and non-brominated flame retardant PC/ABS blend with a well-balanced combination of flowability, impact strength, and enhanced heat resistance, suitable for diverse applications.


General

Form

  Resin Pellets

Physical

Nominal Value

Test Method

Density / Specific Gravity

1.18 g/cm³

ASTM D792

Specific Gravity, Color

1.22 g/cm³

ASTM D792

Water Absorption(24 hr;23 °C)

0.10 %

ASTM D570

Moisture Absorption at Equilibrium(24 hr;23 °C)

0.40 %

ASTM D570

Linear Mold Shrinkage, Flow(Thickness; 3.2 mm)

0.4 - 0.6 %


Linear Mold Shrinkage, Transverse(Thickness; 3.2 mm)

0.4 - 0.6 %


Melt Flow(2.16 kg;260 °C;Condition E)

10 g/10min

ASTM D1238

Hardness, Rockwell R

123

ASTM D785

Mechanical

Nominal Value

Test Method

Tensile Strength, Yield

62.0 MPa

ASTM D638

Elongation at Break

40 %

ASTM D638

Flexural Yield Strength

102 MPa

ASTM D790

Flexural Modulus

2650 MPa

ASTM D790

Izod Impact, Notched

Temperature; 23 °C

Temperature; -30 °C


534 J/m

160 J/m

ASTM D256

Dart Drop, Total Energy

Temperature; -30 °C;0.5 in Tup;150 in/sec

Temperature; 23 °C;0.5 in Tup;150 in/sec


54.0 J

61.0 J

ASTM D3763



Thermal

Nominal Value

Test Method

CTE, Flow(Temperature; -30 - 30 °C;2.7 mm/mm)

72.0 µm/m-°C

ASTM D696

CLTE, Transverse(Temperature; -30 - 30 °C;2.7 mm/mm)

72.0 µm/m-°C

ASTM D696

Thermal Conductivity

0.200 W/m-K

ASTM C177

Deflection Temperature

Thickness; 6.4 mm;Pressure; 0.46 MPa

Thickness; 3.2 mm;Pressure; 1.8 MPa

Thickness; 6.4 mm;Pressure; 1.8 MPa


104 °C

90.0 °C

95.0 °C

ASTM D648

Vicat Softening Point

112 °C

ASTM D1525

UL RTI, Electrical

85.0 °C

UL 746B

UL RTI, Mechanical with Impact

85.0 °C

UL 746B

UL RTI, Mechanical without Impact

85.0 °C

UL 746B

Flammability, UL94

Thickness; 1.49 mm;Thickness; 0.03 in

Thickness; 2.48 mm;Thickness; 0.03 in


V-0

5VB

UL 94

Oxygen Index

32 %

ASTM D2863

Hot Wire Ignition, HWI

60 - 120 sec

UL 746A

Electrical

Nominal Value

Test Method

Volume Resistivity

1.00e+17 ohms ·cm

ASTM D257

Surface Resistance

> = 1.00e+16 Ohms

ASTM D257

Dielectric Constant

Frequency; 50 - 60 Hz

Frequency; 100 Hz


3.0

3.0

ASTM D150

Dielectric Strength(Thickness; 3.2 mm)

19.4 kV/mm

ASTM D149

Dissipation Factor

Frequency; 100 Hz

Frequency; 50 - 60 Hz


0.0049

0.0050

ASTM D150

Arc Resistance(D48/50)

60 - 120 sec

ASTM D495

Comparative Tracking Index

400 - 600 V

UL 746A

High Amp Arc Ignition, HAI

> = 120 arcs

UL 746A

High Voltage Arc-Tracking Rate, HVTR

25.4 - 80.0 mm/min

UL 746A



Processing

Nominal Value

Injection Molding


Drying Temperature

80 - 90 °C

Drying Time

3 - 4 hrs

Drying Time, Cumulative

8 hrs

Maximum Moisture Content

0.04 %

Melt Temperature

245 - 275 °C

Nozzle Temperature

245 - 275 °C

Front - Zone 3 Temperature

245 - 275 °C

Middle - Zone 2 Temperature

220 - 265 °C

Rear - Zone 1 Temperature

220 - 255 °C

Mold Temperature

60 - 80 °C

Back Pressure

0.3 - 0.7 MPa

Screw Speed

40 - 70 rpm

Shot to Cylinder Size

30 - 80 %

Vent Depth

0.038 - 0.076 mm




Inquiry

Scan the qr codeclose
the qr code