Modified PC/ABS Polymer Plastic Raw Material PC/ABS Alloy Particles

Dongguan Forever Co.,Ltd is the manufacture of the China origin cheap UV stablized PC polycarbonate Granules Polymer Resin.

MC8100-XH, a modified plastic, has better properties than pure PC and ABS, such as improved impact resistance, heat resistance, and hardness. Easy for injection molding, extrusion, and blow molding processing.


General

Form                                        Resin Pellets

Physical

Nominal Value

Test Method

Density / Specific Gravity

1.13 g/cm³

ASTM D792

Molding Shrinkage, Flow(3.2 mm)

0.40 - 0.70 %

Internal Method

Water Absorption(24 hr)

0.10 %

ASTM D570

Water Absorption, Equilibrium(23 °C)

0.40 %

ASTM D570

Mechanical

Nominal Value

Test Method

Tensile Modulus(50 mm/min)

2060 MPa

ASTM D638

Tensile Strength, Yield(50 mm/min;Type I)

52.0 MPa

ASTM D638

Tensile Elongation, Yield(50 mm/min;Type I)

5.0 %

ASTM D638

Tensile Elongation, Break(50 mm/min;Type I)

100 %

ASTM D638

Flexural Modulus(1.3 mm/min;50 mm;Span)

2060 MPa

ASTM D790

Flexural Strength, Yield(1.3 mm/min;50 mm;Span)

77.0 MPa

ASTM D790

Notched Izod Impact

-30 °C

23 °C


430 J/m

530 J/m

ASTM D256

Instrumented Dart Impact, Total Energy

-30 °C

23 °C


47.0 J

54.0 J

ASTM D3763

Thermal

Nominal Value

Test Method

Deflection Temperature Under Load, Unannealed

0.45 MPa;3.2 mm

1.8 MPa;3.2 mm


123 °C

104 °C

ASTM D648

CLTE, Flow(-40 - 40 °C)

8.1E-5 cm/cm/°C

ASTM E831

Thermal Conductivity

0.20 W/m-K

ASTM C177



Processing

Nominal Value

Drying Temperature<Extrusion Blow Molding>

100 - 110 °C

Drying Time

3 - 4 hrs

Drying Time, Cumulative<Extrusion Blow Molding>

24 hrs

Minimum Moisture Content<Extrusion Blow Molding>

0.04 %

Maximum Moisture Content<Extrusion Blow Molding>

0.04 - 0.05 %

Melt Temperature, Parison

245 - 260 °C

Barrel - Zone 1 Temperature<Extrusion Blow Molding>

240 - 250 °C

Barrel - Zone 2 Temperature<Extrusion Blow Molding>

240 - 255 °C

Barrel - Zone 3 Temperature<Extrusion Blow Molding>

240 - 255 °C

Barrel - Zone 4 Temperature<Extrusion Blow Molding>

240 - 255 °C

Adapter - Zone 5 Temperature<Extrusion Blow

Molding>

245 - 260 °C

Head - Zone 6 - Top Temperature<Extrusion Blow

Molding>

245 - 260 °C

Head - Zone 7 - Bottom Temperature<Extrusion Blow

Molding>

245 - 260 °C

Screw Speed <Extrusion Blow Molding>

20 - 50 rpm

Extruder Feed Zone Temperature<Extrusion Blow

Molding>

60 - 80 °C

Mold Temperature<Extrusion Blow Molding>

40 - 90 °C

Die Temperature<Extrusion Blow Molding>

250 - 265 °C