Injection Moldable PC/ABS Blend Halogen-free Flame Retardant V0 PC/ABS Alloy Particles
Dongguan Forever Co.,Ltd is the manufacture of the China origin cheap UV stablized PC polycarbonate Granules Polymer Resin
RCY6214-XH resin is a versatile PC/ABS blend resin that can be easily injected into molds. It is specially formulated with a flame retardant that does not contain bromine or chlorine. This resin is environmentally friendly as it includes 35% post consumer recycle content. It has been notably tested and achieved a UL-94 V0 rating, indicating excellent fire-resistant properties, even at a thickness of 1.5 mm. This resin is designed for a wide range of applications that demand a combination of good flow characteristics and impact resistance.
General | ||||
Form |
| |||
Feature |
| Non-Brominated & Non- Chlorinated Flame Retardant | Non-Chlorinated Pcr | |
Usage | ||||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.18 | ASTM D792 | ||
Water Absorption(24 hrs;23 °C) | 0.1 % | ASTM D570 | ||
Melt Flow Rate[MFR](260 °C;2.16 kgf) | 21 g/10min | ASTM D1238 | ||
Mechanical | Nominal Value | Test Method | ||
Izod Impact, Notched(23 °C) | 500 J/m | ASTM D256 | ||
Instrumented Dart Impact, Total Energy(23 °C) | 50 J | ASTM D3763 | ||
Notched Izod Impact Strength(notched;80*10*3;23 °C 0) | 51 kJ/m² | ISO 180/1A | ||
Tensile Stress, Yield(50 mm/min;Type I) | 60 MPa | ASTM D638 | ||
Tensile Stress, Break(50 mm/min;Type I) | 47 MPa | ASTM D638 | ||
Tensile Strain, Yield(50 mm/min;Type I) | 4 % | ASTM D638 | ||
Tensile Strain, Break(50 mm/min;Type I) | 40 % | ASTM D638 | ||
Tensile Modulus(50 mm/min) | 2500 MPa | ASTM D638 | ||
Flexural Stress, Yield(1.3 mm/min;50 mm;span) | 90 MPa | ASTM D790 | ||
Flexural Modulus(1.3 mm/min;50 mm;span) | 2400 MPa | ASTM D790 | ||
Resin PelletsThermal | Nominal Value | Test Method |
UL Recognized ≥ 1.5 mm ≥ 1.2 mm ≥ 0.3 mm | V-0 V-1 HB | UL 94 |
Vicat Softening Temperature(Rate B/50) | 100 °C | ASTM D1525 |
Heat Deflection Temperature[HDT], Unannealed 3.2 mm;1.82 MPa 0.45 MPa;6.4 mm 1.82 MPa;6.4 mm | 85 °C 101 °C 92 °C | ASTM D648 |
CTE, Flow(-40°C to 60°C) | 7.1e-05 1/°C | ASTM E831 |
CTE, XFlow(-40°C to 60°C) | 7.2e-05 1/°C | ASTM E831 |
Relative Temp Index, Elec | 85 °C | UL 746B |
Relative Temp Index, Mechanical with Impact | 85 °C | UL 746B |
Relative Temp Index, Mechanical without Impact | 85 °C | UL 746B |
Electrical | Nominal Value | Test Method |
Hot-wire Ignition, HWI( ≥ 3 mm) | PLC 2 | UL 746A |
Processing | Nominal Value | |
Drying Temperature<Injection> | 80 - 90 °C | |
Drying Time<Injection> | 3 - 4 hrs | |
Drying Time, Cumulative<Injection> | 8 hrs | |
Maximum Moisture Content<Injection> | 0.04 % | |
Melt Temperature<Injection> | 245 - 275 °C | |
Nozzle Temperature<Injection> | 245 - 275 °C | |
Front, Zone 3 Temperature<Injection> | 245 - 275 °C | |
Middle, Zone 2 Temperature<Injection> | 220 - 265 °C | |
Rear, Zone 1 Temperature<Injection> | 220 - 255 °C | |
Mold Temperature<Injection> | 60 - 80 °C | |
Back Pressure<Injection> | 0.3 - 0.7 MPa | |
Screw Speed <Injection> | 40 - 70 rpm | |
Shot To Cylinder Size<Injection> | 30 - 80 % | |
Vent Depth <Injection> | 0.038 - 0.076 mm |