Glass Reinforced Thermal Stability for Electronic And Electrical Applications PA6 Nylon 6 Resin

Dongguan Forever Co.,Ltd is the manufacture of the china origin cheap UV stablized PC polycarbonate Granules Polymer Resin

S223-KG7-XH can maintain strong strength and stiffness at higher temperatures. 

PA6 plastic still has hygroscopicity after molding, and its degree mainly depends 

on the material composition, wall thickness, and environmental conditions.


General

Form                                        Resin Pellets

Filler                                         35 % Glass Fiber

Feature                                     Good Thermal

Usage                                        Electrical

Physical                                                                                 Nominal Value                                       Test Method

Density, dry                                                                           1.41 g/cm³                                              ISO 1183

Dry: Molding Shrinkage, Across Flow                                 1.0 %                                                       ISO 294-4

Dry: Molding Shrinkage, Flow                                             0.20 %                                                     ISO 294-4

Dry: Water Absorption, Saturation(23 °C)                           5.5 %                                                      ISO 62

Dry: Water Absorption, Equilibrium(50% RH;23 °C)           1.5 %                                                       ISO 62



Mechanical

Nominal Value

Test Method

Dry: Tensile Modulus

11500 MPa

ISO 527-2

Condition: Tensile Modulus

7550 MPa

ISO 527-2

Dry: Tensile Stress, Break

210 MPa

ISO 527-2

Condition: Tensile Stress, Break

140 MPa

ISO 527-2

Dry: Tensile Strain, Break

3.5 %

ISO 527-2

Condition: Tensile Strain, Break

5.8 %

ISO 527-2

Dry: Flexural Modulus

9400 MPa

ISO 178

Dry: Flexural Stress

270 MPa

ISO 178

Dry: Charpy Notched Impact Strength

-30 °C

23 °C


11 kJ/m²

14 kJ/m²

ISO 179 1eA

Condition: Charpy Notched Impact Strength

-30 °C

23 °C


11 kJ/m²

18 kJ/m²

ISO 179 1eA

Dry: Charpy Unnotched Impact Strength

-30 °C

23 °C


74 kJ/m²

89 kJ/m²

ISO 179 1eU

Condition: Charpy Unnotched Impact Strength

-30 °C

23 °C


74 kJ/m²

95 kJ/m²

ISO 179 1eU

Thermal

Nominal Value

Test Method

Dry: Heat Deflection Temperature, Unannealed

0.45 MPa

1.8 MPa


260 °C

247 °C


ISO 75-2/B

ISO 75-2/A

Dry: Melting Temperature(10 °C/min)

260 °C

ISO 11357-3

Dry: CLTE, Flow

2.0E-5 cm/cm/°C

ISO 11359-2

Dry: CLTE, Transverse

6.0E-5 cm/cm/°C

ISO 11359-2




Inquiry

Scan the qr codeclose
the qr code