Good Aesthetics Good Dimensional Stability Heat Resistant Polyamide 6 Nylon 6 Material

Dongguan Forever Co.,Ltd is the manufacture of the china origin cheap UV stablized PC polycarbonate Granules Polymer Resin


PA6-G30-XH is a reinforced Polyamide 6 (Nylon 6) material, incorporating a 30% glass fiber filler. 

Notable characteristics of PA6-G30-XH include its flame retardant properties, excellent aesthetics, 

dimensional stability, resistance to high temperatures, and high strength. 


This material finds common use in various applications such as appliances, 

electrical/electronic components, engineering/industrial parts, and tools.


General

Form                                        Resin Pellets

Filler                                         30 % Glass Fiber

Feature                                     Good Dimensional            Good Surface Appearance  Good Thermal

Uses

  Appliance Components            Electrical                           

  Power                                        Mechanical Parts

Physical                                                                                 Nominal Value                                       Test Method

Density / Specific Gravity                                                     1.36 g/cm³                                             ISO 1183

Molding Shrinkage, Across Flow                                         0.90 %                                                    ISO 2577

Molding Shrinkage, Flow                                                     0.30 %                                                    ISO 2577

Water Absorption, Equilibrium(50% RH;23 °C)                   1.8 %                                                      ISO 62

Ash Content                                                                         30 %                                                       ISO 3451-1

Mechanical                                                                            Nominal Value                                      Test Method

Tensile Stress                                                                        185 MPa                                                ISO 527-2/10

Tensile Strain, Break                                                             3.0 %                                                      ISO 527-2/10

Flexural Modulus(2 mm/min)                                              8200 MPa                                               ISO 178

Flexural Stress(2 mm/min)                                                   270 MPa                                                 ISO 178

Notched Izod Impact Strength(23 °C)                                 14 kJ/m²                                                 ISO 180

Thermal                                                                                 Nominal Value                                      Test Method

Heat Deflection Temperature, Unannealed

0.45 MPa                                                                            255 °C                                                     ISO 75-2/B

1.8 MPa                                                                               250 °C                                                     ISO 75-2/A

Flame Rating                                                                          HB                                                            UL 94

Electrical                                                                                Nominal Value                                       Test Method

Volume Resistivity                                                               1.0e+15 ohms ·cm                                  IEC 60093



Processing

Nominal Value

Drying Temperature - Desiccant Dryer<Injection>

90 - 110 °C

Drying Time - Desiccant Dryer<Injection>

4.0 - 6.0 hr

Rear Temperature<Injection>

260 - 275 °C

Middle Temperature<injection>

270 - 280 °C

Front Temperature<Injection>

280 - 290 °C

Processing Temp, Melt<Injection>

270 - 290 °C

Mold Temperature<Injection>

50 - 120 °C

Injection Rate<Injection>

Moderate-Fast