High Quality Factory Resin Polymer Heat Stabilized PA6 Nylon Polyamide Particles

Dongguan Forever Co.,Ltd is the manufacture of the China origin cheap UV stablized PC polycarbonate Granules Polymer Resin


PROTECT A 20 V35 BK 25-XH is a flame retardant polyamide 6, reinforced with 35% glass fiber and heat stabilized, 

specifically designed for injection molding applications. It meets the stringent UL 94 V-0 flame retardant rating 

while also exhibiting excellent mechanical properties. 


This grade is specifically suited for the production of 

insulating parts for electrical devices, as well as thin parts exposed to stress.


General

Form                                        Resin Pellets

Filler                                         35 % Glass Fiber

Uses                                         Connector                          Wire & Cable Applications  Electrical

Physical                                                                                 Nominal Value                                       Test Method

Density / Specific Gravity                                                     1.46 g/cm³                                             ISO 1183

Water Absorption(24 hr, 23°C)                                            0.6 %                                                      ISO 62

Molding shrinkage, parallel(72 hr, 23°C, 50% RH)              0.25 %

ISO 294-4, ISO 2577

Molding shrinkage, normal(72 hr, 23°C, 50% RH)              1 %

ISO 294-4, ISO 2577



Mechanical

Nominal Value

Test Method

Tensile Modulus

1 mm/min/dry

1 mm/min/conditioned


12500 MPa

8200 MPa

ISO 527-1/-2

Stress at break

dry

conditioned


175 MPa

110 MPa

ISO 527-1/-2

Strain at break

dry

conditioned


2.1 %

3.2 %

ISO 527-1/-2

Flexural Modulus

2 mm/min/dry

2 mm/min/conditioned


11000 MPa

7500 MPa

ISO 178

Flexural Strength

2 mm/min/dry

2 mm/min/conditioned


260 MPa

200 MPa

ISO 178

C harpy Impact Strength, Unnotched

dry; 23 ℃

conditioned; 23

-30 ℃


60 kJ/m²

70 kJ/m²

55 kJ/m²

ISO 179 1eU

C harpy Notched Impact Strength

dry; 23 ℃

conditioned; 23

-30 ℃


10 kJ/m²

12 kJ/m²

8 kJ/m²

ISO 179 1eA

Unnotched Izod Impact Strength(23 ℃)

10 kJ/m²

ISO 180/1U

Notched Izod Impact Strength(23 ℃)

12 kJ/m²

ISO 180/1A



Thermal

Nominal Value

Test Method

Melting Temperature(10°C/min)

263 °C

ISO 11357-1

Temp. of deflection under load(1.8 MPa)

244 °C

ISO 75

Flammability

0.75 mm

1.5 mm

3 mm


V-0

V-0

V-0

UL 94

Glow-Wire Flammability, GWFI

0.75 mm

1.5 mm

3 mm


960 °C

960 °C

960 °C

IEC 60695-2-12

Glow Wire Ignition Temperature [GWIT](1.5 mm)

725 °C

IEC 60695-2-13

Oxygen Index

31 %


Electrical

Nominal Value

Test Method

Volume Resistivity

1E+11 ohms ·cm

IEC 62631-3-1

Surface Resistivity

1E+014 Ohms

IEC 62631-3-1

Comparative Tracking Index(Solution A)

400 V

IEC 60112

Dielectric Strength(1 mm)

32 kV/mm

IEC 60243-1

Processing


Nominal Value

Drying Temperature


80 °C

Drying Time


2 - 4 h

Suggested Max Moisture


0.2 %

Rear Temperature


265 - 275 °C

Middle Temperature


270 - 280 °C

Front Temperature


280 - 290 °C

Mould Temperature<Injection>


60 - 90 °C




Inquiry

Scan the qr codeclose
the qr code