PA6 PA6-TC

Forever-Plastics, manufacture of plastics raw materials for thermal conductive PA6 resin with glass fiber reinforced and UL94 HB flammability rating at 0.75mm and 1.6mm. Excellent electrical and flow properties, good forming nature to process and high thermal conductivity. RoHS and Reach Compliant.

Forever-Plastics, manufacture of plastics raw materials for thermal conductive PA6 pellets 

with glass fiber reinforced and UL94 HB flammability rating at 0.75mm and 1.6mm. 


Excellent electrical and flow properties, 

Good forming nature to process 

High thermal conductivity. 

RoHS and Reach Compliant.

                                                  

TYPICAL PROPERTIES

STANDARD

UNIT

TYPICAL VALUE

Physical Property

Specific Gravity

ISO1183

g/cm3

1.52

Mold Shrinkage

ISO294

%

0.3-0.7

Water Absorption(23,4hr)

ISO62

%

0.5

Mechanical Property

Tensile Strength

ISO527

MPa

60

Tensile Strain at Break

ISO527

%

5.0

Flexural Strength

ISO178

MPa

88

Flexural Modulus

ISO178

MPa

  4800

Notched Izod Impact Strength

ISO180

KJ/m2

5

Thermal Property

 

HDT (1.8MPa)

ISO75

150

Flammability(0.75mm)

UL94

--

HB

Flammability(1.6mm)

UL94

--

HB

     Thermal conductivity

ASTM E1461

W/mk

2.0

UL746

         RTI(Elec) (0.75mm)

 UL746

80

         RTI(Elec) (1.6mm)

 UL746

80

         RTI(Imp) (0.75mm)

 UL746

80

         RTI(Imp) (1.6mm)

 UL746

80

         RTI(Str) (0.75mm)

 UL746

80

         RTI(Str) (1.6mm)

 UL746

80

CTI

              -

 UL746

-

2

HAI

            0.75mm

 UL746

-

0

HAI

           1.6mm

 UL746

-

0

HWI

           0.75mm

 UL746

-

4

HWI

           1.6mm

 UL746

-

4

 Processing Condition

Barrel Zone Temp.

Zone 1

240260

Zone 2

240260℃

Zone 3

230250℃

Nozzle Temperature

230250℃

Mold Temperature

60-100℃

Pre-dry Requirements

120℃, 2~6hr

 


 

 


Previous:PA6 PA6-TC-2 Next:PC XH-19HF-12

Inquiry