Thermal Conductive Nylon 6 Granules PA6 Raw Material Plastic Manufacturer

Dongguan Forever Co.,Ltd is the manufacture of the China origin cheap UV stablized PC polycarbonate Granules Polymer Resin

Product Description

3-8896/WT/V-0-XH type PA6 resin can make strong, hard parts. Isotropic shrinkage properties. Inherently flame retardant. Application areas: Automotive industry, textile machinery, instruments and precision engineering. Typical parts: Electrical and electronic industry parts.

General

Form                                        Resin Pellets

Feature

Thermally

  Conductive(Isolation)

Physical

Nominal Value

Test Method

Density / Specific Gravity

1.78 g/cm³

ISO 1183

Linear Mold Shrinkage

0.7 - 0.9 %


Mechanical

Nominal Value

Test Method

Tensile Strength

55.0 MPa


Elongation at Break

2.00 %


Modulus of Elasticity

5500 MPa


Flexural Strength(Strain 2.6 %)

80.0 MPa


Flexural Modulus

4500 MPa


C harpy Impact Unnotched(23 °C)

28 kJ/m²

ISO 179 1eU

Thermal

Nominal Value

Test Method

Thermal Conductivity, In Plane(Hot Disk;Parallel 60x60x3 1.20 W/m-K

mm)

Maximum Service Temperature, Air



Continuous

90.0 °C


Short Term

130 °C


Electrical

Nominal Value

Test Method

Volume Resistivity(10V)

> = 1.00e+13 ohms ·cm


Surface Resistance(10 V)

> = 1.00e+13 Ohms




Processing

Nominal Value

Nozzle Temperature

270 - 280 °C

Zone 1

250 - 270 °C

Barrel - Zone 2 Temperature

270 - 290 °C

Barrel - Zone 3 Temperature

280 - 300 °C

Melt Temperature

270 °C

Mold Temperature

70.0 - 110 °C

Drying Temperature


Time 10 - 16 hr

75.0 °C

Time 4 - 6 hr

105 °C