High Quality Plastics Raw Materials Thermal Conductive Plastic PA6 With Natural Color

Dongguan Forever Co.,Ltd is the manufacture of the China origin cheap UV stablized PC polycarbonate Granules Polymer Resin

200 A TC-I-10-XH type PA6 resin can make strong, hard parts. Isotropic shrinkage properties. Inherently flame retardant. Application areas: Automotive industry, textile machinery, instruments and precision engineering. Typical parts: Electrical and electronic industry parts.

General

Form                                        Resin Pellets

Feature                                     High Reflection

Thermally

  Conductive(Isolation)

Physical

Nominal Value

Test Method

Density / Specific Gravity

1.51 g/cm³

ASTM D792

Mechanical

Nominal Value

Test Method

Tensile Strength, Break

75.8 MPa

ASTM D638

Elongation at Break

2.0 %

ASTM D638

Tensile Modulus

6890 MPa

ASTM D638

Flexural Strength

131 MPa

ASTM D790

Flexural Modulus

6890 MPa

ASTM D790

Izod Impact, Notched(Thickness; 3.2 mm)

26.7 J/m

ASTM D256

Izod Impact, Unnotched(Thickness; 3.2 mm)

427 J/m

ASTM D4812

Thermal

Nominal Value

Test Method

Thermal conductivity through plane(through-plane)

0.500 W/m-K

ASTM E1530

Thermal conductivity in plane(in-plane)

1.10 W/m-K

ASTM E1461

Deflection Temperature(Pressure; 1.8 MPa)

171 °C

ASTM D648

Electrical

Nominal Value

Test Method

Surface Resistivity per Square

> = 1.00e+14 Ohms

ASTM D257

Dielectric Strength(In Oil;Short Term)

15.1 kV/mm

ASTM D149

Processing


Nominal Value

Melt Temperature


243 - 279 °C

Mold Temperature


54.4 - 93.3 °C

Drying Temperature(Time 2 hr)


82.2 °C

Moisture Content


0.20 %

Dew Point


-17.8 °C

Injection Pressure


68.9 - 103 MPa