Multipurpose Injection Molding of High Viscosity Lubricated Nylon 6 Resin

Dongguan Forever Co.,Ltd is the manufacture of the china origin cheap UV stablized PC polycarbonate Granules Polymer Resin

F136-E1-XH has a low melting point and a wide process temperature range. It has better impact resistance and solubility than PA66, but also stronger moisture absorption.


General

Form                                        Resin Pellets

Feature                                     High Viscosity

  Nucleated


Physical

Nominal Value

Test Method

Density / Specific Gravity

1.13 g/cm³

ISO 1183

Viscosity Number

245 cm³/g

ISO 307

Melt Viscosity(260 °C)

2.25E+6 mPa · s

Internal Method

Mechanical

Nominal Value

Test Method

Coefficient of Friction, Dynamic

0.80

ISO 8295

Coefficient of Friction, Static

1.4

ISO 8295

Film Thickness - Tested

50 µm


Tensile Modulus(50 mm/min)

465 MPa

Internal Method

Tensile Stress - MD, Yield

34.0 MPa

ISO 527-3

Tensile Stress - MD, Break

94.0 MPa

ISO 527-3

Tensile Elongation, Break, MD

350 %

ISO 527-3

Trouser Tear - Parallel

32.0

ISO 6383-1

Thermal

Nominal Value

Test Method

CLTE, Flow

9.0E-5 cm/cm/°C

ISO 11359-2

Specific Heat Capacity

1550 J/kg/°C


Average Specific Heat Capacity(20 - 150 °C)

2250 J/kg/°C


Optical

Nominal Value

Test Method

Clarity

85 %

Internal Method



Processing

Nominal Value

Cylinder Zone 1 Temp. <Extrusion>

270 °C

Cylinder Zone 2 Temp. <Extrusion>

270 °C

Cylinder Zone 3 Temp. <Extrusion>

270 °C

Cylinder Zone 4 Temp. <Extrusion>

270 °C

Die Temperature<Extrusion>

270 °C

Chill Roll Temperature<Extrusion>

110 °C