PC HF1110RXH
Dongguan Forever Co.,Ltd is the manufacture of the china origin cheap UV stablized PC polycarbonate Granules Polymer Resin
HF1110-XH is a high flow grade polymer with an easy mold release version. It is specifically designed for applications that require thin wall lighting lenses, data storage components, and safety eyewear lenses.
General | ||||
Form | Resin Pellets | |||
Feature | Excellent Processability | |||
Appliances Lighting Applications Automotive Lighting | ||||
Usage | Electronic Displays | Pharmaceuticals | Sporting Goods
| |
Automotive Exterior
| Automotive Interior
| Constraction | ||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.20 g/cm³ | ASTM D792 | ||
Melt Mass-Flow Rate, MFR(300 °C;1.2 kg) | 25 g/10min | ASTM D1238 | ||
Molding Shrinkage, Flow(3.2 mm) | 0.50 - 0.70 % | Internal Method | ||
Mechanical | Nominal Value | Test Method | ||
Tensile Strength, Yield(50 mm/min;Type I) | 62.0 MPa | ASTM D638 | ||
Tensile Strength, Break(50 mm/min;Type I) | 65.0 MPa | ASTM D638 | ||
Tensile Elongation, Break(50 mm/min;Type I) | 120 % | ASTM D638 | ||
Flexural Modulus(1.3 mm/min;50 mm;Span) | 2300 MPa | ASTM D790 | ||
Flexural Strength, Yield(1.3 mm/min;50 mm;Span) | 93.0 MPa | ASTM D790 | ||
Notched Izod Impact(23 °C) | 640 J/m | ASTM D256 | ||
Instrumented Dart Impact, Energy at Peak(23 °C) | 54.0 J | ASTM D3763 | ||
Tensile Impact Strength(Type S) | 378 kJ/m² | ASTM D1822 | ||
Thermal | Nominal Value | Test Method | ||
Deflection Temperature Under Load, Unannealed(1.8 MPa;3.2 mm) | 126 °C | ASTM D648 | ||
RTI Elec | 130 °C | UL 746 | ||
RTI Imp | 130 °C | UL 746 | ||
RTI Str | 130 °C | UL 746 | ||
Flame Rating(1.1 mm) | V-2 | UL 94 | ||