Non-Chlorinated/Brominated Flame Retardant Polycarbonate-Forever Plastics

Dongguan Forever Co.,Ltd has manfactured the non-chlorinated/brominated flame retardant polycarbonate(PC) granules

Dongguan Forever Co.,Ltd has manfactured the polycarbonate(PC) granules with the characteristics as below


Injection grade 

Non-chlorinated/brominated 

10% glass fiber filled. 

UV stabilized 

UL94 [email protected] rating 

F1 


The resin or pellets polycarbonate(PC) is widely used in the applications of lighting,electronic displays....


Physical

Nominal Value

Test Method

Density / Specific Gravity

1.25g/cm³

ASTM D792;

ISO1183

Melt Mass-Flow Rate, MFR(300 °C;1.2 kg)

10g/10min

ASTM D1238

Molding Shrinkage, Flow(3.2 mm)

0.40 - 0.60 %

Internal Method

Outdoor Suitability

F1

UL 746C

Mechanical

Nominal Value

Test Method

Tensile Modulus

5 mm/min

 

3600 MPa

3500 MPa

 

ASTM D638

ISO 527-2/1

Tensile Strength, Break

5 mm/min;Type I

 

62.0 MPa

60.0 MPa

 

ASTM D638

ISO 527-2/5

Tensile Elongation, Break

5 mm/min;Type I

 

6.0 %

6.0 %

 

ASTM D638

ISO 527-2/5

Flexural Modulus

1.3 mm/min;50 mm;Span

2 mm/min

 

3200 MPa

3500 MPa

 

ASTM D790

ISO 178

Flexural Stress, at Yield(2 mm/min)

120 MPa

ISO 178

Flexural Stress, Yield(1.3 mm/min;50 mm;Span)

110 MPa

ASTM D790

Notched Izod Impact

-30 °C

23 °C

-30 °C;80*10*3 mm

23 °C;80*10*3 mm

 

70 J/m

90 J/m    8.0 kJ/m²

10 kJ/m²

 

ASTM D256

ASTM D256

ISO 180/1A

ISO 180/1A

 

Thermal

Nominal Value

Test Method

Deflection Temperature Under Load, Unannealed 1.8 MPa;3.2 mm

 

135 °C

 

 

ASTM D648

Ball Pressure Test(123 - 127 °C)

Pass

ISO 11359-2

Flame Rating

0.75 mm

1.5 mm

3 mm

3 mm

 

V-2

V-0

5VA

5VB

UL 94

Glow Wire Flammability Index(0.75 mm)

960 °C

IEC 60695-2-12

 

 

Processing

Nominal Value

Drying Temperature<Injection>

120 °C

Drying Time<Injection>

2.0 - 4.0 hr

Suggested Max Moisture<Injection>

0.02%

Hopper Temperature<Injection>

60 - 80 °C

Rear Temperature<Injection>

270 - 300 °C

Middle Temperature<injection>

280 - 310 °C

Front Temperature<Injection>

290 - 320 °C

Nozzle Temperature<Injection>

280 - 310 °C

Processing Temp, Melt<Injection>

290 - 320 °C

Mold Temperature<Injection>

80 - 120 °C