Injection Molding Grade Engineer Plastic PBT Resin GF30 Plastic Raw Materials

Dongguan Forever Co.,Ltd is the manufacture of the China origin cheap UV stablized PC polycarbonate Granules Polymer Resin


The WF0061iQ-XH compound is made from Poly butylene terephthalate (PBT) resin using ELCRIN iQ upcycling technology, 

which incorporates a minimum of 25% Post-Consumer Recycling (PCR) weight content and 30% glass fiber. 


This grade offers additional advantages such as being Non-Chlorinated, Non-Brominated Flame Retardant, 

having a UL94V0 and 5VA Flame Rating, and displaying excellent chemical resistance. 


It is an ideal option for various applications that require a more sustainable flame retardant (FR) and PBT solution.


General

Form


Resin Pellets


Filler


30 % Glass Fiber



Feature


Good Hardness                 

25 % Pcr

Non-Brominated & Non- Chlorinated Flame Retardant


Chemical Resistant           

Non-Chlorinated

  Pcr

Uses                                         Automotive

  Consumer

  Electrical

Physical

Nominal Value

Test Method

Density / Specific Gravity


1.56

1.56 g/cm³


ASTM D792

ISO 1183

Water Absorption(23 °C;saturated)

0.23 %

ISO 62-1

Moisture Absorption(50% RH;23 °C)

0.09 %

ISO 62

Melt Volume Rate, MVR(5 kg;MVR at 250 °C)

16 cm³/10 min

ISO 1133



Mechanical

Nominal Value

Test Method

Izod Impact, Unnotched



23 °C

570 J/m

ASTM D4812

80*10*4;23 °C

37 kJ/m²

ISO 180/1U

Izod Impact, Notched



23 °C

72 J/m

ASTM D256

-30 °C

55 J/m

ASTM D256

80*10*4;23 °C

7 kJ/m²

ISO 180/1A

80*10*4;-30 °C

6 kJ/m²

ISO 180/1A

Instrumented Dart Impact, Total Energy(23 °C)

6 J

ASTM D3763

Tensile Stress, Yield



5 mm/min;Type I

105 MPa

ASTM D638

5 mm/min

108 MPa

ISO 527

Tensile Stress, Break



5 mm/min;Type I

105 MPa

ASTM D638

5 mm/min

108 MPa

ISO 527

Tensile Strain, Yield



5 mm/min;Type I

2 %

ASTM D638

5 mm/min

2 %

ISO 527

Tensile Strain, Break



5 mm/min;Type I

2 %

ASTM D638

5 mm/min

2 %

ISO 527

Tensile Modulus



5 mm/min

1.1E+04 MPa

ASTM D638

1 mm/min

1.1E+04 MPa

ISO 527

Flexural Stress, Yield



1.3 mm/min;50 mm;span

165 MPa

ASTM D790

2 mm/min

175 MPa

ISO 178

Flexural Stress, break



1.3 mm/min;50 mm;span

165 MPa

ASTM D790

2 mm/min

175 MPa

ISO 178

Flexural Modulus



1.3 mm/min;50 mm;span

9600 MPa

ASTM D790

2 mm/min

1.0E+04 MPa

ISO 178



Thermal

Nominal Value

Test Method

UL Recognized

≥ 0.8 mm

≥ 3 mm


V-0

5VB

UL 94

Glow Wire Ignition Temperature [GWIT]

3 mm

1.5 mm

0.8 mm


800 °C

775 °C

750 °C

IEC 60695-2-13

Glow Wire Flammability Index

3 mm

1.5 mm

0.8 mm


960 °C

960 °C

960 °C

IEC 60695-2-12

Heat Deflection Temperature[HDT], Unannealed

3.2 mm;1.82 MPa

0.45 MPa;3.2 mm


200 °C

214 °C

ASTM D648

CTE, Flow(-40 - 40 °C)

2.4E-05 1/°C

ASTM E831

CTE, XFlow(-40 - 40 °C)

8.0e-05 1/°C

ASTM E831

Ball Pressure Test(125°C +/- 2°C)

PASSES

IEC 60695-10-2

Relative Temp Index, Elec

75 °C

UL 746B

Relative Temp Index, Mechanical with Impact

75 °C

UL 746B

Relative Temp Index, Mechanical without Impact

75 °C

UL 746B

Electrical

Nominal Value

Test Method

Hot-wire Ignition, HWI

≥ 0.8 mm

≥ 3 mm


PLC 1

PLC 0

UL 746A

High Amp Arc Ignition, HAI( ≥ 0.8 mm)

PLC 0

UL 746A

Comparative Tracking Index

600 V

IEC 60112